有色冶金渣制备胶凝材料研究现状与展望

郭利杰,张雷,李文臣

Progress and Prospects of the Preparation of Cementitious Materials Based on Nonferrous Metallurgical Slags

Lijie GUO,Lei ZHANG,Wenchen LI

图14 高温下碱激发铜渣及水泥铜渣砂浆质量损失[30] CCM0-水泥；CCM5-95%水泥+5%铜渣；CCM10-90%水泥+10%铜渣；CCM15-85%水泥+15%铜渣；AACM6-碱激发铜渣，碱浓度为6 M；AACM8-碱激发铜渣，碱浓度为8 M；AACM10-碱激发铜渣，碱浓度为10 M；AACM12-碱激发铜渣，碱浓度为12 M

Fig.14 Mass loss of alkali activated copper slag and cement with copper slag mortar at high temperature[30]